Hffr Compound for Communication Cable Fiber Cable

Model NO.: POHF-0701
Trademark: EPCHEM
Transport Package: Aluminum Foil Bag
Specification: polyolefin
Origin: Shanghai
HS Code: 3902900090
Model NO.: POHF-0701
Trademark: EPCHEM
Transport Package: Aluminum Foil Bag
Specification: polyolefin
Origin: Shanghai
HS Code: 3902900090
Introduction
EPchem® POHF-0701 is polyolefin based material containing inorganic flame retardant, antioxidant, lubricant, etc., produced by mixing, plasticizing and then pelletizing. It is particularly suitable for sheath of communication cables, optical cables and so on.
POHF-0701 is excellent in mechanical properties, flame retardant performance, resistance to UV, good processability.

Characteristics
Properties Unit Standard Typical value* Test method
Density g/cm3 ≤1.50 1.482 GB/T 1033.1-2008
Tensile strength MPa ≥10 12 GB/T 1040-2006
Elongation at break % ≥150 180 GB/T 1040-2006
Mechanical properties after ageing ºC×h 110×168 110×168 GB/T 2951.12-2008
Rentention Rate of Tensile strength % ≥80 85
Rentention Rate of Elongation at break % ≥80 86
Hot deformation (90ºC*4h) % ≤50 Pass GB/T 8815-2008
Brittleness temperature by impact (-25ºC) Invalidation ≤15/30 Pass GB/T 5470-2008
Volume resistivity (20ºC) W.m ≥1×1010 2.3×1012 GB/T 1410-2006
Dielectric strength MV/m ≥18 28 GB/T 1408.1-2006
Oxygen index % ≥30 38 GB/T 2406.2-2009
Smoke density Flame   ≤100 68 GB/T 8323-2008
Non-flame   ≤250 220
Content of halogen acid gas mg/g ≤5 0.9 GB/T 17650.1-1998
PH   ≥4.3 5.9 GB/T 17650.2-1998
Conductivity μs/mm ≤10 1
Toxicity index   ≤5 1.1 NES 713-1985
*The data in the list above is typical value rather than the guarantee value.

Processing
POHF-0701 has good processing performance, can be well processed using PVC and Polyethylene standard extrusion screw, preferring a low compression ratio (1.2 ~ 1.8) screw for the best extrusion effect. In general we recommend the following processing conditions:
  • Extruder L/D: 20~25
  • Filter (mesh): 30~60
  • Temperature setting:
     Zone1    Zone2    Zone3   Zone4    Zone5      Die
    110ºC   120ºC   135ºC  145ºC   150ºC   150~165ºC
The above temperatures are for reference only, but should be adjusted depending on specific equipment.
POHF-0701 can be extruded by squeeze die but also squeeze tube die.
POHF-0701 includes black and natural color. Users are free to add color masterbatches to natural color material. The suggested weight ratio is 1.5% or so.

Storage
These compounds must be stored under the following conditions:
  1. closed and undamaged bags
  2. ambient temperature does not exceed 45ºC
  3. avoid direct exposure to sunlight and weathering
  4. shelf life:12 months.
Package
To be packed in aluminum foil bag inside and kraft paper bags outside, 25kg net each; or damp-proof cabinets on pallet, 1000kg net each.



Hffr Compound for Communication Cable Fiber Cable

Hffr Compound for Communication Cable Fiber Cable
The workshop:
Hffr Compound for Communication Cable Fiber Cable

Package :

Hffr Compound for Communication Cable Fiber Cable
  Introduction
EPchem® POHF-0701 is polyolefin based material containing inorganic flame retardant, antioxidant, lubricant, etc., produced by mixing, plasticizing and then pelletizing. It is particularly suitable for sheath of communication cables, optical cables and so on.
POHF-0701 is excellent in mechanical properties, flame retardant performance, resistance to UV, good processability.

Characteristics
Properties Unit Standard Typical value* Test method
Density g/cm3 ≤1.50 1.482 GB/T 1033.1-2008
Tensile strength MPa ≥10 12 GB/T 1040-2006
Elongation at break % ≥150 180 GB/T 1040-2006
Mechanical properties after ageing ºC×h 110×168 110×168 GB/T 2951.12-2008
Rentention Rate of Tensile strength % ≥80 85
Rentention Rate of Elongation at break % ≥80 86
Hot deformation (90ºC*4h) % ≤50 Pass GB/T 8815-2008
Brittleness temperature by impact (-25ºC) Invalidation ≤15/30 Pass GB/T 5470-2008
Volume resistivity (20ºC) W.m ≥1×1010 2.3×1012 GB/T 1410-2006
Dielectric strength MV/m ≥18 28 GB/T 1408.1-2006
Oxygen index % ≥30 38 GB/T 2406.2-2009
Smoke density Flame   ≤100 68 GB/T 8323-2008
Non-flame   ≤250 220
Content of halogen acid gas mg/g ≤5 0.9 GB/T 17650.1-1998
PH   ≥4.3 5.9 GB/T 17650.2-1998
Conductivity μs/mm ≤10 1
Toxicity index   ≤5 1.1 NES 713-1985
*The data in the list above is typical value rather than the guarantee value.

Processing
POHF-0701 has good processing performance, can be well processed using PVC and Polyethylene standard extrusion screw, preferring a low compression ratio (1.2 ~ 1.8) screw for the best extrusion effect. In general we recommend the following processing conditions:
  • Extruder L/D: 20~25
  • Filter (mesh): 30~60
  • Temperature setting:
     Zone1    Zone2    Zone3   Zone4    Zone5      Die
    110ºC   120ºC   135ºC  145ºC   150ºC   150~165ºC
The above temperatures are for reference only, but should be adjusted depending on specific equipment.
POHF-0701 can be extruded by squeeze die but also squeeze tube die.
POHF-0701 includes black and natural color. Users are free to add color masterbatches to natural color material. The suggested weight ratio is 1.5% or so.

Storage
These compounds must be stored under the following conditions:
  1. closed and undamaged bags
  2. ambient temperature does not exceed 45ºC
  3. avoid direct exposure to sunlight and weathering
  4. shelf life:12 months.
Package
To be packed in aluminum foil bag inside and kraft paper bags outside, 25kg net each; or damp-proof cabinets on pallet, 1000kg net each.



Hffr Compound for Communication Cable Fiber Cable

Hffr Compound for Communication Cable Fiber Cable
The workshop:
Hffr Compound for Communication Cable Fiber Cable

Package :

Hffr Compound for Communication Cable Fiber Cable
 

Drill Bits

Drill Bits,Iron Bit,Drill Set,Auger Bit

SHANGQIU DING LIAN INTERNATIONAL TRADE CO. ,LTD , https://www.dingqitools.com

Posted on